1.Temperature (°C)From the diagram below, analyze a 40%Ni-60% Cu alloy at 1250°C.a.)What phases are present?b.)What are their chemical compositions?C.)If our system contains 100 grams, how much of each phase is present?1300MM CM120020-Liquida Liquid.112 3 4 5½a30203840Composition (wt% Ni)9 10 11 12½ 4½50

Compositon: 40%Ni-60%CuTemperature: 1250 °C

1. Temperature (°C) From the diagram below, analyze a 40%Ni-60% Cu alloy at 1250°C. a.) What phases are present? b.) What are their chemical compositions? If our system contains 100 grams, how much of each phase is present? 1300 MM CM 1200 20 Liquid a Liquid- 3 a 4 5 6 30 8 9 10 11 : 3 4 40 Composition (wt% Ni) 5 50

1. Temperature (°C) From the diagram below, analyze a 40%Ni-60% Cu alloy at 1250°C. a.) What phases are present? b.) What are their chemical compositions? If our system contains 100 grams, how much of each phase is present? 1300 MM CM 1200 20 Liquid a Liquid- 3 a 4 5 6 30 8 9 10 11 : 3 4 40 Composition (wt% Ni) 5 50

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

Help me please
Temperature (°C) Based on the Ti-Al phase diagram (important for standard commercial alloy Ti-6Al- 4V) shown below, identify a) the type of reaction (e.g., peritectic) of the marked points (1) and b) list the phases before and after the reactions. 10 20 Weight percent aluminum 30 40 50 60 70 80 90 100 1800 1700 1670°C (1) 1600 L 1500 1400 a (ẞTi) 1300 1285 y-TiAl 1200 1100 1125 لسسسلسسسل 1000 Ti, Al (L10) 900 ር? 882°C 800 (aTi) (D019) 700 600 500 0 10 20 Ti Superlattice structures -TiAl, 665°C 660.452°C TiAl₂ aTiAl3 (Al). 20 30 40 50 60 70 80 90 100 Atomic percent aluminum PM Al
help pls A two-phase phase diagram is shown. Answer the following questions t -1300 1500+ Temperature 1100 0 34 54! 166 482 80 Composition of Ni % 20 What is the composition (in % Cu) of the solid phase corresponding to the red dot in between the solidus and liquidus lines in the phase diagram? Just write the number. Do not write the % symbol. Question 17 2.33 100 An alloy is being made with 66% Ni and 34% Cu. When it is cooled from 1500°C to the temperature corresponding to the red dot in the phase diagram, how many kg of liquid is present in the mixture?
Temperature (°C) 700 600 0 500 400 300 0 (AI) a 5 a+L 10 Composition (at% Cu) 10 20 a +0 L 30 Composition (wt% Cu) 20 0+ L 0 (CuAl₂) 40 30 50 1200 1000 800 600 Temperature (°F) a) For the alloy represented by the phase diagram above, what is the wt% content of eutectic if an alloy of 2.5 wt% Cu is cooled very slowly from the molten state to 300°C? b) What phases are present in 2.5 wt% Cu material if it is quenched from 550°C?
Question 9 An Ag-Cu alloy contains 25% a and 75% B at 600"C. The composition of the overall alloy is approximately 1000 L+B 800 a /8.87. 28-12 9224 a +8 500 972 400 Ag 10 20 30 40 50 60 70 80 90 Cu Cu (by weight) O A. 73.5% Cu OB. 65.8% Cu OC. 89.6% Cu D 80.2% Cu
Given the Cu-Zn phase diagram below, determine the amount of the phase/s present of a 75 wt% Zn -25 wt% Cu alloy for the following temperatures. Indicate the required composition for each temperature in the diagram. Round off your final answers up to two decimal places. Show your solutions completely and neatly and follow the table format below, Temperature Phase/s present Phase composition Relative amount 600 °C 570 °C y+ L 700 1200 8+L L 600 P 598°C 560°C 570 |1000 e + L y +e 500 60 68.6 70 74.3 75 78.2 80 90 Composition (wt % Zn) Temperature (°C) ta Temperature (°F)
Composition lat% N 40 60 100 1600 2800 1500 1453 C 2600 Liquid 1400 Solidus line Liquidua line 2400 1300 1200 2200 1100 1085 C 2000 1000 20 40 100 Composition (wt N (NO What is the amount for each phase in 1kg of a 50% Ni-50% Cu alloy at temperatures of 1400, 1300, or 1200 degrees C for point A and point B? Temperature ('C) Temperature ("F)
4. For the A-B alloy the phase diagram below, use the lever rule to find the amount of liquid and solid states and their compositions at Temperature T. Let Cx = 25%B, C =40%B, Cy = 60 %B Complete solubility of two metals in liquid and solid states (Ni -Cu ,Sb - Bi) TA M EM T EMa T Cy A B Concentration of B in A www.substoch com Temperature
For a copper-silver alloy of composition 9.7 wt% Ag-90.3 wt% Cu and at 775°C (1425°F) (see Animated Figure 9.7) do the following: (a) Determine the mass fractions of a and phases. Mass fraction a = i Mass fraction = i (b) Determine the mass fractions of primary a and eutectic microconstituents. Mass fraction a primary = i Mass fraction eutectic = i (c) Determine the mass fraction of eutectic a. Mass fraction a eutectic = i
3. How many kilograms of nickel must be added to 1.75kg of copper to yield a liquidus temperature of 1300°C? Temperature (°C) 1400 1300 1200 1100 1085C 0 (Cu) 20 Liquid Liquidus line a+L 60 40 Composition (wt% Ni) 1453°C Solidus line 80 100 (Ni)
please show work and formulas so that i may learn the process correctly. if you use a table please mention which table was used. thank you so much. 2. Fill in the blank cells of this table: T( C) P(kPa) u(kJ/kg) Phase description 175 2524.5 325 4000 325 Saturated liquid
Consider Al- Cu system below. When Al-40%Cu is heated above 600°C and cooled slowly to a temperature of 545°C . Answer the following. Use the values of composition given in the phase diagram , no estimation .Each has two marks. 700 1200 600 L a + L 6 +L 548 1000 500 (CUAL) a + 6 800 400 600 300 5.65 10 20 30 32.7 40 50 52.5 (AI) Composition (wt % Cu) a. Percentage of the pro-eutectic phase present (% no decimal places) b. Composition of the pro- eutectic phase present (in %Cu one decimal place) c. What is the percentage of larger eutectic component present (% no decimal places) Temperature (°C) Temperature (°F)