Problem No.2 A bar of circular cross-section is subjected to alternating tensile forces varying from a minimum of 200 kN to a maximum of 500 kN. It is to be manufactured of a material with an ultimate tensile strength of 900 MPa and an endurance limit of 700 Mpa (the stress below which a material can tolerate repeated load cycles without failure). Determine the diameter of bar using safety factors of 3.5 related to ultimate tensile strength and 4 related to endurance limit and a stress concentration factor of 1.65 for fatigue load. Use Goodman straight line as basis for design.

Problem No.2 A bar of circular cross-section is subjected to alternating tensile forces varying from a minimum of 200 kN to a maximum of 500 kN. It is to be manufactured of a material with an ultimate tensile strength of 900 MPa and an endurance limit of 700 Mpa (the stress below which a material can tolerate repeated load cycles without failure). Determine the diameter of bar using safety factors of 3.5 related to ultimate tensile strength and 4 related to endurance limit and a stress concentration factor of 1.65 for fatigue load. Use Goodman straight line as basis for design.

Elements Of Electromagnetics

7th Edition

ISBN:9780190698614

Author:Sadiku, Matthew N. O.

Publisher:Sadiku, Matthew N. O.

ChapterMA: Math Assessment

Section: Chapter Questions

Problem 1.1MA

See similar textbooks

Similar questions

You are in charge of designing a new fixture for a “universal testing machine” that will attach a tensile specimen to the machine using a clevis—a U-shaped piece with holes drilled through the two arms—and a cylindrical pin that passes through the clevis and the specimen. If the maximum load exerted by the machine is 30 kN and the pin is to be made of some sort of steel, what is the minimum pin diameter needed to ensure that the shear stress in the pin does not exceed 600 MPa? Assume that the steel has similar elastic properties to pure Fe.
A sample test rod made of a ferrous material of 0.5 in. diameter was tested for tensile strength with the gauge length of 2.5 in. The following observations were recorded: Final length = 3.15 in; Final diameter = 0.275 in; Yield load = 7650 lb. and Ultimate load = 10375 lb. (a) Calculate: 1. yield stress, 2. ultimate tensile stress, 3. percentage reduction in area, and 4. percentage elongation. (b) What specific material, if any, is similar to this tested rod? Refer to AT7 and AT8. (c) This same material is then used as a tension member 55 inches long and is subjected to a maximum load of 6000 lb, repeated but not reversed. (d) Solve part (c) if the total elongation is not to exceed 0.025 in.? 1. %3D
One piece is made of a metal alloy with a yield limit of 180 MPa. At a certain point in the part that is under a flat state of tension, it is known that one of the main stresses is compressive and is half the magnitude of another main stress, which is tensile. Specify the maximum magnitude that the traction component can have, considering that the project requires the adoption of a safety factor 2.0 against flow, according to the criteria of Von Mises and Tresca.
450-mm-long AISI 1020 steel rod is subjected to a tensile load of 55 kN. The allowable tensile stress is 140 MPa and the allowable total elongation is not to exceed 0.2 mm. Calculate the required rod diameter. The proportional limit is 175 MPa.
a)Draw the stress-strain curve of a ductile material such as that of a ductile steel and discuss the various regions of the curve. Explain the difference between a ductile and brittle material and the concept of ductility and its measurement. b)A machine part 10 mm thick, having the dimensions shown in the figure, is to be subjected to cyclic loading. If the maximum stress is limited to 60 MPa, determine the allowable force P. Approximate the stress concentration factors form the graph given. Where might a potential fracture occur?
What wall thickness in mm is required for a 634 mm diameter cylinder under an internal pressure of 18 MPa? Use a design stress of 80 MPa?
A mild steel rod having a stress of 50 Mpa and having a diameter of 20 mm What is the force applied on it.
In a standard tensile test a steel rod of 7/8 in. in diameter is subjected to a tension force of 17 kips. Determine the ratio of the shear modulus to the modulus of elasticity of a material whose Poisson's ratio is 0.25.
A tensile stress is applied along the long axis of a cylindrical brass rod thathas a diameter of 10 mm. Given the Poisson’s ratio for brass is 0.35,determine the magnitude of the load required to produce a 2.5 x 10-3 mmchange in diameter if the deformation is entirely elastic. Take the Young’sModulus (E) for brass as 10.1x104 MPa.
Sketch a tensile member with (a) a rectangular crosssection, (b) a solid circular cross section, and (c) a circulartubecross section, and label the dimensions symbolically (e.g.,label the radius for the solid circular case). For each member, write out the definition of engineering stress in terms of the actual dimensions of the component. If therectangular member has dimensions of width and thicknessequal to 1 cm 0.3 cm, what would be the radius of a solidcircular member such that the stress is equal for an equaltensile load? If a tube has an outer radius equal to that ofthis same solid cylinder, what is the maximum inner radiussuch that the stress does not exceed 200% of the stress inthe solid cylinder?
See the set of bars for made of a material that has a yield strength of 350 MPa, determine the minimum h1 and h2 dimensions required. Apply a safety factor F.S. = 1.5 without flow. Each bar is 12 mm thick
Problem 4: 6.43. The simple expressions for Rockwell hardness num- bers in Table 6.9 involve indentation, 1, expressed in millimeters. A given steel with a BHN of 235 is also measured by a Rockwell hardness tester. Using a 16 -in.-diameter steel sphere and a load of 100 kg, the indentation t is found to be 0.062 mm. What is the Rockwell hardness number? Solution: