Derive the lever rule for the amount in weight percent of each phase in two-phase regions of a binary phase diagram. Use a phase diagram in which two elements are completely soluble in each other.
Obtain the weight percentages of the liquid and solid phases in any two phase region of binary equilibrium phase diagram by the help of lever rule.
Explanation of Solution
Let the phase diagram of two elements
The lever equations can be obtained by the help of weight balances. The first equation of lever rule is derived by taking the sum of the weight fraction of liquid and solid phase as 1.
Write the sum of the phases as,
Here, weight fraction of liquid and solid phase is
Derive the second equation of the lever rule by a using a weight balance of
Write the weight balance by considering
Substitute
Rewrite Equation (II) to get weight fraction of solid phase.
Substitute
Equations (III) and (IV) are called as lever rule equations for solid and liquid phase respectively.
Hence, the lever rule equations are
Want to see more full solutions like this?
Chapter 8 Solutions
Foundations of Materials Science and Engineering
- BINARY PHASE DIAGRAMS Please only answer parts d and e as the rest have been solved. Show full detailed explanation to answers with diagrams if necessary a)(i) What is the melting point of pure Mg?(ii) What is the maximum solubility of Mg in Pb and at what temperaturedoes this occur? (b) A 50 wt.% Pb-50wt% Mg alloy is slowly cooled from 700 °C to 400 °C.(i) At what temperature does the first solid phase form?(ii) What is the composition of this solid phase?(iii) At what temperature does all the liquid solidify?(iv) What is the composition of the last remaining liquid phase?(v) What is the freezing range? (c) What is the mass fraction of solid and liquid of a 60 wt.% Mg alloy at atemperature of 500 °C.(d) Draw and label the microstructure of an 80 wt.% Mg alloy at 600 °C.(e) A Mg-Pb alloy of mass 5.5 kg has a composition just slightly below thesolubility limit of 200 °C.(i) What mass of lead is in the alloy?(ii) If the alloy is heated to 350 °C how much more lead can be dissolvedin…arrow_forwardCalculate the weight fraction for phases at point B? what are those phases? Is there any eutectic rection? How many phases are present in this diagram? Cu-Ni system T(°C) TA 1300 -L (liquid): A tie ļine liquidus L +a Тв EB solidus (solid) 1200 TD ID 20 3032 35: 4043 50 Ca wt% Niarrow_forwardAccording to the following graph, two samples of 1080 steel are cooled from the eutectoid temperature, one at a cooling rate of 250°C/s and the other at a cooling rate of 7.27x10-8 °C/s. Specify the phases obtained and explain their formation from thermodynamic and kinetic perspectives. Also, briefly describe their formation. Draw the microstructure of the phases obtained. Sıcaklık (C) 800 700 600 500 400 300 200 100 0 10 1 T M(başlama) M(% 50) M(% 90) 10 M+O -Otektoid Sıcaklık 10² Zaman (s) % 50 10³ 104 105arrow_forward
- Use the phase diagrams for Cu-Ni and Cu-Ag systems below to answer the question: Based on the mechanism, would you expect a solution containing 80 wt% Cu to be stronger if the remaining 20% of the alloy was Ni or Ag? Briefly explainarrow_forwardA copper-nickel alloy contains 38% by weight of Cu and 62% by weight of Ni and is at 1330 ° C. Using the figure, answer the following questions:a) What is the percentage by weight of copper in the solid and liquid phases at this temperature?b) What percentage by weight of the alloy is liquid and what percentage is solid?arrow_forwardFor an alloy containing 20 wt % Ag, refer to the Cu-Ag phase diagram given in the Figure: What is the melting point of Cu in °C? What are the relative amounts(in %) of the existing phases at 900°C? Define the Eutectic point in terms of °C and the composition % of Ag.arrow_forward
- 5. (a) Construct the phase diagram for zinc and magnesium system using the following data: Melting point of Mg is 665°C Melting point of Zn is 500 °C One eutectic point at 350 °C with 20% of Zn (i) (ii) (iii) (b) Describe what happens when the mixture of 40% mole of Zn is cooled to from 650 °C to 200 °C?arrow_forwardReferring to Figure 1, please answer the following [NOTE: SHOW YOUR WORK on Figure 1]:a. provide the specific name for the phase boundary lines denoted by A and B. b. identify the phases present at equilibrium in the phase fields denoted by C, D, and E. c. identify the specific name for the point denoted by F. d. What is the maximum solid solubility of Mg in Al? At what temperature does it occur? e. An Al-Mg alloy (10 wt% Mg, 90 wt% Al) is heated slowly (to insure equilibrium) from a temperature of 200 C: i. At what temperature does the first liquid phase form? ii. What is the composition of the liquid phase at the temperature in part i.? iii. At what temperature does complete melting (no solid phase remaining) occur? iv. What is the composition of the last solid remaining prior to complete melting? f. Using the equilibrium phase diagram of Figure 1, identify the phases present, their compositions, and their relative mass fractions at equilibrium for a 70 wt% Mg – 30 wt% Al…arrow_forwardFigure 2 refers to the phase diagram for silver and tin. Label the regions (1) to (5) Temperature, 0/°C 1000 800 600 400 200 0 Liquid 2 Ag,Sn 60 a 20 40 80 Mass percentage Ag/% 100 Question 6: What will be observed when liquids of composition of 40% Ag are cooled to 200 K? When will it begin to precipitate? When will it become solid?arrow_forward
- Given the equilibrium phase diagram (a) below, briefly describe the mechanisms of precipitation hardening/strengthening of an aluminium alloy making reference to the transitions shown in (b) below to X, X to A, X to D, A to B and A to C. а +0 D B Time (a) (b) - anedua Temperaturearrow_forward3) You see Al-Cu phase diagram below and two microstructures (A and B) having the same nominal composition of 3 percent Cu. In these microstructures, matrix is a and spheres refer to CuAl₂ particles. In A and B, the size of big particles are the same. a) For the same volume constant, if we heat treat the both microstructures at T₁ for a long time, is there any changes in both microstructures? If so, what is that? And is the changes the same for both A and B? Is the rate of changes the same for A and B? Draw the final microstructures of A and B if any changes occur you think so. Temperature a AI 2 I 4 a +CuAl2 1 6 Copper,% CuAl2 αarrow_forward4. The figure below shows the phase diagram for a hypereutectoid plain carbon steel. Assume that point c is slightly above 723 °C and point d is slightly below 723 °C. i. Explain the structure at points a, b, c, and d on the diagram. ii. Determine the wt% of proeutectoid cementite at point c. iii. Determine the wt% of eutectoid cementite at point d. Temperature (°C) 1100 900 700 500 300 100 a + Y R 0 100% Fe 0.02 1.0 Fe, C 1.2 2.0 Fe,C Fe, C Pearlite 3.0 4.0 Weight percent carbon y+ Fe, C 723°C a + Fe, C 1 5.0 Fe,C 1 6.0 6.7arrow_forward
- Elements Of ElectromagneticsMechanical EngineeringISBN:9780190698614Author:Sadiku, Matthew N. O.Publisher:Oxford University PressMechanics of Materials (10th Edition)Mechanical EngineeringISBN:9780134319650Author:Russell C. HibbelerPublisher:PEARSONThermodynamics: An Engineering ApproachMechanical EngineeringISBN:9781259822674Author:Yunus A. Cengel Dr., Michael A. BolesPublisher:McGraw-Hill Education
- Control Systems EngineeringMechanical EngineeringISBN:9781118170519Author:Norman S. NisePublisher:WILEYMechanics of Materials (MindTap Course List)Mechanical EngineeringISBN:9781337093347Author:Barry J. Goodno, James M. GerePublisher:Cengage LearningEngineering Mechanics: StaticsMechanical EngineeringISBN:9781118807330Author:James L. Meriam, L. G. Kraige, J. N. BoltonPublisher:WILEY