The enthalpy of activation for viscous flow in soda lime glass in the temperature range 700K to 800K.
Answer to Problem 9.1P
The enthalpy of activation for viscous flow in soda lime glass in the temperature range 700K to 800K is
Explanation of Solution
Given:
Temperature range is
Concept used:
Write the expression for viscosity as function of temperature.
Here,
Calculation:
Refer to Figure 9.3 “The temperature dependence of the viscosity of silica glass
Substitute
Substitute
Divide equation (2) by equation (3).
Take logarithm on both sides.
Substitute
Conclusion:
Thus, the enthalpy of activation for viscous flow in soda lime glass in the temperature range 700K to 800K is
Want to see more full solutions like this?
Chapter 9 Solutions
Materials Science And Engineering Properties
- 6 A steel pipe with a 50 mm outside diameter and a 43.75 'mm inside diameter surrounds a solid brass rod 37.5 mm in diameter as shown. Both materials are joined to a rigid cover plate at each end. The assembly is free to expand longitudinally. The assembly is stress free at a temperature of 27°C. For steel, Young's modulus is 200 GN/m², and the coefficient of linear thermal expansion is 11.7x10-6 1/°C. For brass, Young's modulus is 93.33 GN/m², and the coefficient of linear thermal expansion is 1.872 x 10-5 1/°C. What is the stress in the steel tube when the temperature is raised to 121°C? brass rod (solid) 37.5 mm diameter steel tube 50 mm outside diameter 43.75 mm inside diameterarrow_forwardWhen a bar is cooled to -5°C, it will develop O(A) No stress OCB) Shear stress OC) Tensile stress O(D) Compressive stressarrow_forwardUsing the isothermal transformation diagram for a 0.45 wt% C steel alloy (Figure 10.40), determine the final microstructure (in terms of just the microconstituents present) AND approximate percentages of the microconstituents that form in a small specimen that has been subjected to the following time-temperature treatments. In each case assume that the specimen begins at 845°C (1550°F), and that it has been held at this temperature long enough to have achieved a complete and homogeneous austenitic structure. (a) Rapidly cool to 250°C (480°F), hold for 10^3 s, then quench to room temperature. (b) Rapidly cool to 700°C (1290°F), hold for 30 s, then quench to room temperature. (c) Rapidly cool to 700°C (1290°F), hold at this temperature for 10^5 s, then quench to room temperature. (d) Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature.arrow_forward
- At 170°C, what is the maximum solubility (a) of Pb in Sn and (b) of Sn in Pb? The lead-tin phase diagram is shown in the Animated Figure 9.8. (a) wt% Pb (b) i wt% Snarrow_forwardthis is about thermal stressarrow_forwardGiven your understanding of what initiates and controls failure in materials, which of the following will increase the failure strength or lifetime of a test piece or component and why? a. Decreasing the difference between the maximum and minimum stress values, as this effects the stress concentration factor b. Decreasing the temperature below the brittle-ductile transition temperature, to make it harder C. Polishing to reduce surface defects Od. Increasing its volume, to give a larger cross sectional area Oe. Increasing the grain size so there are less grain boundaries to initiate failurearrow_forward
- Materials Science And Engineering PropertiesCivil EngineeringISBN:9781111988609Author:Charles GilmorePublisher:Cengage Learning